Beattie, Deborah L. published the artcileRAFT aqueous dispersion polymerization of 4-hydroxybutyl acrylate: effect of end-group ionization on the formation and colloidal stability of sterically-stabilized diblock copolymer nanoparticles, Recommanded Product: 2-Phenylethanethiol, the publication is Polymer Chemistry (2022), 13(5), 655-667, database is CAplus.
A series of all-acrylic poly(2-hydroxyethyl acrylate)x-poly(4-hydroxybutyl acrylate)y (PHEAx-PHBAy) diblock copolymer nanoparticles were prepared via an efficient one-pot RAFT aqueous dispersion polymerization protocol using either a carboxylic acid-functionalized RAFT agent (HOOC-PHEAx-PHBAy) or a morpholine-functionalized RAFT agent (Mo-PHEAx-PHBAy). The pH-dependent colloidal stability of the resulting sterically-stabilized nanoparticles was assessed by dynamic light scattering and aqueous electrophoresis. The HOOC-PHEA73-PHBA217 nanoparticles exhibited reversible flocculation below pH 5.1, whereas the Mo-PHEA76-PHBA160 nanoparticles flocculated above pH 5. Moreover, the HOOC-PHEA73-PHBA217 nanoparticles proved to be sensitive to added salt, with incipient flocculation occurring in the presence of 20-60 mM KCl owing to charge screening. Thus, such nanoparticles require end-group ionization to confer colloidal stability via electrosteric stabilization. However, reducing the PHBA/PHEA molar ratio and/or increasing the PHEAx stabilizer DP, leads to more efficient steric stabilization and hence enhanced colloidal stability. A series of HOOC-PHEA73-PHBA104-421 nano-objects prepared at pH 7 were characterized by visual inspection, DLS studies and shear-induced polarized light imaging. Discrepancies between these characterization techniques indicated that the worms and vesicles were unstable with respect to dilution TEM studies were conducted after covalent stabilization of the nano-objects using glutaraldehyde (GA). More specifically, TEM studies of GA-crosslinked HOOC-PHEA73-PHBA243 and HOOC-PHEA73-PHBA421 nano-objects indicated the presence of spheres in both cases when crosslinked at 0.1% weight/weight and either worms or vesicles resp., when crosslinked at 10-20% weight/weight Finally, HOOC-PHEA73-PHBA265 nano-objects were examined by variable temperature oscillatory rheol.; thermoreversible sphere/worm and worm/vesicle transitions were observed between 2 and 50°.
Polymer Chemistry published new progress about 4410-99-5. 4410-99-5 belongs to alcohols-buliding-blocks, auxiliary class Thiol,Benzene, name is 2-Phenylethanethiol, and the molecular formula is C8H10S, Recommanded Product: 2-Phenylethanethiol.
Referemce:
https://en.wikipedia.org/wiki/Alcohol,
Alcohols – Chemistry LibreTexts